• HOME
  • about us
  • Products
    • Alkyd resin
      • Architectural paints and coatings
        • Gloss and semi gloss paint
          • BAL 108 WS-70
          • BAL 116 WS-70
          • BAL 117 WS-70
          • BAL 118 WS-70
          • BAL 133 WS-70
        • Primer and surfacer
          • BAL 104 WS-70
        • Clear coat and lacquer
          • BAL 108 WS-70
          • BAL 116 WS-70
          • BAL 133 WS-70
        • Pigment paste
          • BAL 106 WS-70
      • Industrial paints and coatings
        • Hammer finish paint
          • BAS 305 X-50
          • BAS 308 X-60
          • BAS 310 X-60
          • BAS 320 X-60
        • Automotive repair paint
          • BAM 203 X-60
          • BAM 208 WSX-55
          • BAM 212 X-60
        • Lacquer, stoving enamel and paint
          • BAS 302 X-60
          • BAS 304 X-60
          • BAS 307 X-60
          • BAS 310 X-60
          • BAS 311 X-65
        • Fast dry paint
          • BAM 203 X-60
          • BAS 305 X-50
          • BAS 308 X-60
          • BAS 320 X-60
        • Metallic structure paint
          • BAM 207 WS-55
        • Anti corrosion primer
          • BAM 207 WS-55
          • BAS 310 X-60
          • BAS 312 X-60
        • Nitro cellulose enamel and paint
          • BAS 302 X-60
          • BAS 304 X-60
          • BAS 307 X-60
          • BAS 311 X-65
          • BMA 401 T-70
        • Nitro cellulose putty and filler
          • BAS 312 X-60
      • Other coatings
        • Wood coatings
          • BAS 302 X-60
          • BAS 304 X-60
          • BAS 307 X-60
          • BAS 310 X-60
          • BAS 311 X-65
          • BMA 401 T-70
        • Amino modified lacquer and clear coat
          • BAS 302 X-60
          • BAS 320 X-60
          • BAS 304 X-60
          • BAS 307 X-60
          • BAS 310 X-60
          • BAS 311 X-65
        • Aerosol can and paint spray
          • BAL 106 WS-70
          • BAL 133 WS-70
          • BAM 203 X-60
          • BAM 208 WSX-55
        • Traffic paints
          • BMA 401 T-70
    • Unsaturated polyester resin
      • Molding
        • BUP 617
        • BUP 621
        • BUP 640
      • Pipes and tanks
        • BUP 620
        • BUP 621
        • BUP 630
        • BUP 660
      • Hand Lay-up
        • BUP 614
        • BUP 615
        • BUP 621
        • BUP 630
      • Marine
        • BUP 630
        • BUP 631
        • BUP 660
      • SMC-BMC
        • BUP 670
        • BUP 672
      • Stone industries
        • BUP 621
        • BUP 623
        • BUP 624
        • BUP 665
        • BUP 690
      • Button
        • BUP 640
      • Others
        • BUP 620
        • BUP 645
        • BUP 665
      • Pultrusion
        • BUP 630
        • BUP 631
        • BUP 660
    • Saturated polyester resins
      • EP-PE
        • EP/PE 510
        • EP/PE 520
        • EP/PE 530
      • PE / TGIC
        • PE/TGIC 550
    • Maleic Resin
      • BMA 401 T-70
    • Driers
      • Driers
        • BD-Ca-5
        • BD-CO-10
        • BD-Pb-32
        • BD-Zr-18
  • Gallery
    • Factory and office
    • exhibitions
  • News
  • Certificates
  • Contact
FARU
EN
BKC-Logo-Final4

BUP 623

Home BUP 623

Ortho Phthalic, Unsaturated Polyester Resins

BUP 623

Unsaturated Polyester Resin

Orthophthalic Polyester Resin

Product Description:

BUP 623 is an un-promoted orthophthalic based unsaturated polyester resin with medium viscosity, limited shrinkage and very good mechanical properties for ambient temperature cure with MEK peroxide.

Characteristics and Advantages:

  • Medium viscosity
  • Limited shrinkage
  • Very good adhesion to glass fibers
  • Very good mechanical properties
  • Outstanding filler binding power
  • Outstanding filler binding power

Uses:

  • Artificial stone
  • Solid surface

Technical Properties:

Physical data in liquid state at 25°C

These data are measured for each lot by our QC lab before its release.

Properties

Unit

Value

Test method

Appearance

NA

Clear

NA

Color

Gardner

Max 1

ASTM D1544

Viscosity (at 25°C)

mPa.s (cP)

500-700

ISO 2555

Density (at 23°C)

g/cm³

1.1448

ASTM D1475

Acid number

mg KOH/g

Max 25

ASTM D1639

Solid content

wt %

65±2

ASTM D1259

Gel time*

min

12-25

ASTM D2471

Curing time

min

7-12

ASTM D2471

Peak exothermic temperature

℃

Max 180

ASTM D2471

Water absorption

wt %

Max 0.3

ISO 62

Flash point (open cup)

℃

22

ASTM D92

* Promoter: 0.5 g Cobalt (1%) in 100 g resin @25 °C

Initiator: 2 g MEKP (50%) in 100 g resin

Typical non-reinforced casting properties

These data are not subject to routine monitoring or part of the specifications; they are only reported for a better product description.

Properties

Unit

Value

Test method

Tensile strength

MPa

Min 50

ISO 527-2

Tensile elongation

%

8.2

ISO 527-2

Tensile modulus

MPa

583

ISO 527-2

Flexural strength

MPa

Min 120

ISO 178

Flexural modulus

MPa

2055

ISO 178

Heat distortion temperature (HDT)

°C

Min 55

ASTM D648

Hardness (Barcol)

NA

Min 40

ASTM D2583

Linear shrinkage (∆L/L)

%

Max 1

ASTM D2566

Product safety and Environmental protection:

The usual protective measures employed during the handling of Unsaturated Polyester Resins should be observed. Further product safety information can be obtained from our Material Safety Data Sheet which is available on request.

 Packaging: 225 kg (net) in steel drums.

Storage: Store in a cool place below 25 °C and away from moisture and direct sunlight. Under above mentioned storage conditions, the shelf life of the resin will be at least 6 months ex-works.

Disclaimer: The information and in particular the recommendations relating to the application and use of Bonyan Kala Chemie products are given in good faith based on our current knowledge and expertise of the products when properly stored, handled and used under normal conditions within their shelf life. In practice, the differences in materials, chemistries and actual site conditions are such that no warranty in respect of merchantability or of fitness for a particular purpose, nor any liability arising out of any legal relationship whatsoever, can be inferred either from this information, or from any recommendations, or from any other advice offered. The proprietary rights of third parties must be observed. All orders are accepted subject to our current terms of sale and delivery. Users should always refer to the most recent issue of the Technical Data Sheet for the product concerned, copies of which will be supplied on request or can be accessed from www.bonyankala.com.